1. Bahan: Bahan cangkerang paip keluli biasanya 20 keluli atau keluli Q235;
2. Bentuk tampalan seramik termasuk jenis kimpalan, jenis mozek,-jenis melengkung sendiri, jenis penguncian sendiri-dovetail, jenis sisipan dan jenis lingkaran;
3. Diameter paip: lebih besar daripada atau sama dengan 100mm;
4. Rintangan suhu: kurang daripada atau sama dengan 300 darjah;
5. Kawasan aplikasi: kuasa elektrik, perlombongan, arang batu, dll.;
6. Saiz: Ketebalan - paip keluli shell 5-12mm, ketebalan seramik lapisan 5-25mm, 10mm biasa;
7. Kelebihan:
(1) High hardness: Rockwell hardness is HRC80-90, the hardness is second only to diamond, far exceeding the wear resistance of wear-resistant steel and stainless steel;
(2) High wear resistance: The wear resistance is equivalent to 266 times that of manganese steel and 171.5 times that of high-chromium cast iron;
(3) Light weight: The density of the ceramic sheet is 3.9g/cm3, which is only half of that of steel, which can greatly reduce the load of the equipment;
(4) High purity: alumina content: Greater than or equal to 95 percent
8. Kaedah sambungan: bebibir, penyambung V-, bahagian kimpalan;
9. Prestasi kos tinggi: di bawah keadaan kerja yang sama, penggunaan paip komposit tampalan seramik adalah lebih sesuai daripada paip komposit dwilogam;
10. Langkah berjaga-jaga: Ia tidak tahan-impak. Beri perhatian kepada anti-perlanggaran semasa pengangkutan dan pemasangan. Secara amnya, pembungkusan tertutup diperlukan untuk pembungkusan, seperti rak pembungkusan atau kotak pembungkusan, dan sesetengahnya dibalut dengan tali jerami. Adalah disyorkan untuk memasang telinga mengangkat.